Item

Type

HJ-2185

HJ-2190

HJ-2195

HJ-2197

NCO% Content

3.5±0.2

4.2±0.2

6.0±0.2

6.5±0.2

Density 25℃/(g/cm³)

1.11

1.11

1.12

1.12

Viscosity 80℃/mpa·s

900-1100

800-1000

700-900

600-800

Appearance at 25℃

Colorless transparent liquid

Mix Temperature ℃

Prepolymer /Moca

85℃/115℃

80℃/115℃

75℃/115℃

75℃/115℃

Gel Time /min

13-18

10-15

6-10

3-5

Vulcanization Time (h)

25-16

25-16

25-16

25-16

Physical Properties

Hardness (Shore A)

85±2

90±2

95±2

97±2

Tensile Strength (Mpa)

25-28

33-38

38-45

40-46

100% Modulus (Mpa)

11-12

14-16

16-18

18-20

300% Modulus (Mpa)

18-20

28-30

38-42

40-43

Elongation at Break (%)

360-420

350-400

280-350

250-300

Tear Strength (KN/m)

60-65

75-85

90-100

95-105

Compression permanent deformation %

4-6

4-6

2-4

2-4

DIN Abrasion loss（mm³）

≤45

≤40

≤40

≤40

Resilience %/25℃

40-45

35-40

28-32

26-30

- Product application : PU Rollers, casters, seals, pistons, classification screens, flotation machine impellers, forklift tires, molds, slurry pump linings and other products.

- Operation details:After vacuum degasing at 75-85 ℃, the prepolymer is mixed with melted MOCA for casting and vulcanization. It is suitable for manual and mechanical operation.

- Storage:Store in a cool and dry place and use up as soon as possible after opening; If it cannot be used up at one time, it shall be sealed with nitrogen; The second opening needs to be used for defoaming, and the original storage period is six months.

- Packing:20kg or 200kg iron drum